Synthesis of Biodegradable Hydrogel Based on H-alginate-g-poly(AMPS)
Mohammad Sadeghi*, Fatemeh Shafiei, Esmat Mohammadinasab, Laleh Mansouri and Hadis Shasavar
Department of Chemistry, Science Faculty, Islamic Azad University, Arak Branch, Arak, Iran
ABSTRACT:
In this article, we synthesize of a novel alginate-based superabsorbent hydrogel via graft copolymerization of 2-acrylamido-2-methylpropanesulfonic acid (AMPS) onto alginate backbones. The polymerization reaction was carried out in an aqueous medium and in the presence of ammonium persulfate (APS) as an initiator and N,N'-methylene bisacrylamide (MBA) as a crosslinker. A proposed mechanism for hydrogel formation was suggested and the structure of the product was established using FTIR and SEM spectroscopies.
KEYWORDS:
Alginate; hydrogel ; 2-acrylamido-2-methylpropanesulfonic acid; grafting
Download this article as:Copy the following to cite this article: Sadeghi M, Shafiei F, Mohammadinasab E, Mansouri L, Shasavar H. Synthesis of Biodegradable Hydrogel Based on H-alginate-g-poly(AMPS). Biosci Biotechnol Res Asia 2014;11(1) |
Copy the following to cite this URL: Sadeghi M, Shafiei F, Mohammadinasab E, Mansouri L, Shasavar H. Synthesis of Biodegradable Hydrogel Based on H-alginate-g-poly(AMPS). Biosci Biotechnol Res Asia 2014;11(1). Available from: https://www.biotech-asia.org/?p=6329 |
This work is licensed under a Creative Commons Attribution 4.0 International License.